{"id":3240,"date":"2017-02-02T11:49:02","date_gmt":"2017-02-02T10:49:02","guid":{"rendered":"https:\/\/samuraischwert.kaufen\/?p=3240"},"modified":"2021-02-02T22:24:55","modified_gmt":"2021-02-02T21:24:55","slug":"damascus-steel-call","status":"publish","type":"post","link":"https:\/\/samuraischwert.kaufen\/en\/samuraischwert\/bestandteile\/die-klinge\/damaszener-stahl-ruf\/","title":{"rendered":"Damascus steel - better than its reputation?"},"content":{"rendered":"

Modern Damascus steel has a mediocre reputation and, unfortunately, usually rightly so! The following section takes a closer look at this topic:\n<\/p>\n

Definition of terms<\/h2>\n

\nDamascus steel, Damascus steel, Damascus steel, Damascus steel. There are many names in circulation for this type of steel.
\nThe name has its origins in the former trading metropolis of Damascus in Syria, where many blades made of this material were traded.
\nHowever, the manufacturing process did not originate there. The process was developed independently in several places around the world, with the oldest discovery dating back to the time of the Celts around 300 BC.
\nDamascus blades are a combination of different types of steel to form a blade. Due to the different alloying elements, these blades have a special pattern after appropriate treatment and this is the special feature of a blade made of Damascus steel.\n<\/p>\n

What are the benefits of the procedure?<\/h2>\n

\nNowadays, the focus is more on the resulting pattern and the individuality of each blade.
\nWhen the process was developed, it was not yet possible to produce steel with evenly distributed components. As a result, steel was often very brittle or too soft. By combining different types of steel, it was possible to compensate for any deficits.\n<\/p>\n

Damascus steel - the superior steel?<\/h2>\n

\nIn the past, this manufacturing method was used to produce blades with superior properties, as it compensated for the lack of quality of the steel used at the time. Nowadays, the basic material available, such as Industrial steel<\/a>much better and this compensation is no longer necessary.\n<\/p>\n

Is this steel completely superfluous today?<\/h2>\n

\nThe basic principle that the aspects of different types of steel complement each other still applies today, of course. Positive effects can still be achieved in the high-end sector, provided the right choice of steel and correct processing are used.
\nWhat makes this steel so popular even today is above all the characteristic pattern on the surface of the blade.\n<\/p>\n

Where does the pattern come from?<\/h2>\n

\nDamascus steel itself does not have its own pattern. When polished, the pattern is barely present. To emphasise the pattern, the blade surface must be etched. The different types of steel then react differently with the acid and the typical Damascus steel pattern is formed.<\/p>\n

\"\"
Polished Damascus steel blade<\/figcaption><\/figure>\n
\"\"
The same blade after treatment<\/figcaption><\/figure>\n
<\/div>\n

\nIf a treated blade is polished, the visual highlighting of the pattern is lost again and the blade must be re-etched if the pattern is to be emphasised again. With the Centreboard care<\/a> of Damascus steel blades, care should therefore be taken to ensure that Uchiko<\/a> with a low abrasive effect are used or completely dispensed with and used exclusively Blade oil<\/a> is used.\n<\/p>\n

The quality of the workmanship makes all the difference<\/h2>\n
\"Blacksmith
A blacksmith at work<\/figcaption><\/figure>\n

As is so often the case in blade production, the processing of the blade is very important. On the one hand, the right types of steel must be combined to achieve positive effects and the processing of the raw material requires a certain amount of skill on the part of the blacksmith.<\/p>\n

High-quality blades made from Damascus steel are definitely worth the money.<\/p>\n

Cheap, mass-produced Damascus steel blades may have an attractive appearance, but from a quality point of view these blades should not be overrated. The quality of these blades is often inferior to that of normal mono-steel blades.\n<\/p>\n

<\/div>\n

The difference to Tamahagane steel<\/h2>\n

\nThere is a widespread misconception that Tamahagane steel<\/a> would be the same as Damascus steel. This is because the processing methods are similar. Both types of steel are usually folded<\/a> and consist of inhomogeneous base material.
\nHowever, Damascus steel is processed in such a way that the inhomogeneity in the steel remains, while Tamahagane is folded so often until the steel is almost homogeneous. Despite the similar starting point, these are two completely different materials.<\/p>\n

Explanatory video on Damascus steel and other types of steel:<\/p>\n